caustic cracking
英 [ˈkɔːstɪk ˈkrækɪŋ]
美 [ˈkɔːstɪk ˈkrækɪŋ]
网络 碱性开裂; 碱腐蚀开裂
双语例句
- Optimization of caustic wash process, strengthened monitoring of critical equipment or application of duplex stainless steel or super stainless steel can mitigate the cracking problems.
优化碱洗工艺、对重点设备加强监测或采用双相不锈钢及超级不锈钢可使腐蚀问题得到缓解。 - Presently, there've been no new breakthroughs in comprehensive utilization of the waste caustic liquid from ethylene cracking both domestically and internationally.
目前，国内外在乙烯裂解废碱液综合利用方面尚无新的突破。 - Study on regeneration for spent caustic of ethylene cracking by chemical precipitation
化学沉淀法再生乙烯裂解废碱液的研究 - The results showed that the corrosion weight loss rate of high Mn steel was distinctly greater than that of medium carbon chromium steel. The high Mn steel caustic embrittlement cracking was distinct in corrosion.
结果表明，高锰钢的平均腐蚀速率显著高于中碳铬合金钢，腐蚀过程中高锰钢有较严重的碱脆开裂现象。 - With an increase of the chromium content in the cast steel, active dissolving corrosion increased, however, tendency of caustic embrittlement cracking decreased.
随着钢中含铬量的增加，试验材料的活性溶解腐蚀失重增大，但碱脆开裂的倾向减少。 - Effect of cold work on the caustic stress corrosion cracking of alloy 800
冷加工对800合金抗碱性应力腐蚀破裂的影响 - Caustic stress corrosion cracking of aloy 800 part 1. the effect of applied potential
800合金的碱性应力腐蚀破裂I.外加电位的影响 - Influence of Some Processing Factors on Susceptibility to Caustic Stress Corrosion Cracking of Modified Alloy 800
某些加工因素对改性800合金碱性应力腐蚀破裂敏感性的影响 - Study of Regeneration Technique for Spent Caustic Liquid from Ethylene Cracking
乙烯裂解废碱液再生技术研究 - Study on two-step treatment of spent caustic water from ethylene cracking
两步沉淀法处理乙烯废碱液的实验研究 - An Investigation on Interface Reaction Regularity for Caustic Stress Corrosion Cracking of Fe-Cr-Ni Alloy
Fe-Cr-Ni合金碱性应力腐蚀破裂界面反应规律的研究 - Spent caustic liquid from ethylene cracking is the waste caustic liquid produced from the caustic scrubbing of cracking gas in ethylene plant.
乙烯裂解废碱液是乙烯装置在裂解气碱洗过程中产生的一股碱性废液。 - With increasing corrosion time the impact toughness of high Mn steel obviously decreased. The major mechanism was effect of the caustic embrittlement cracking.
随着热强碱腐蚀时间的延长，高锰钢的冲击韧度明显降低，碱脆开裂是造成高锰钢冲击韧度下降的主要原因。 - Effect of NaOH concentration and alo_2~-species on caustic stress corrosion cracking of a low alloy steel at 260 ℃
NaOH浓度和AlO2~-离子对低合金钢高温碱脆的影响 - The author analyzed factors which caused reactor SCC from materical, stess, media and clarified mechanism of reactor caustic embrittlement and reasons for four cracking rules.
从材料、应力、介质三方面分析了引起尿塔应力腐蚀开裂的要素，阐明了尿塔碱脆的机理和出现四种不同开裂形式的原因。